Low-Fusing Porcelain Glaze Application on 3Y-TZP Surfaces can Enhance Zirconia-Porcelain Adhesion

Abstract

The aim of this study was to assess whether surface treatment improves zirconia-porcelain adhesion. The 3Y-TZP blocks were cut into squares, then polished and sintered. The zirconia surface treatments were performed as follows: no treatment (C); tribochemical silica coating (TBS); glaze application + hydrofluoric acid etching (GA); glaze application + hydrofluoric acid etching + silanization (GAS); deposition of silica nanofilm (NF). After treatments, veneering porcelain cylinders (3.3 x 3.3 mm) were built up on all specimens and fired. Then the specimens were subjected to thermal cycling (6000 cycles), and subjected to shear test. Fractures were analyzed by stereomicroscopy and SEM. Data were statistically analyzed by 1-way ANOVA and Tukey's test (5%). Zirconia-porcelain bond strength was affected by the ceramic surface treatments (p=0.0001). GA (19.5±3 MPa) and GAS (16.2±4 MPa) recorded the highest bond strength values, while control group had the lowest bond value (10.1±4 MPa). Adhesive failure of the samples predominated. Therefore, glaze application as 3Y-TZP treatment before veneering porcelain stratification may enhance zirconia-porcelain adhesion.

Key Words:
surface treatment; zirconia ceramics; bond strength; nanofilm

Fundação Odontológica de Ribeirão Preto Av. do Café, S/N, 14040-904 Ribeirão Preto SP Brasil, Tel.: (55 16) 3602-3982, Fax: (55 16) 3633-0999 - Ribeirão Preto - SP - Brazil
E-mail: bdj@forp.usp.br